The development of efficient strategies for the removal of heavy metal ions from aqueous solutions is rapidly demanded as these contaminants are very toxic and carcinogenic and show detrimental effects on the living creatures. The main focus of the current study is on the preparation and assessment of electrospun adsorptive nanofiber membranes for the removal of toxic Ni(II) and Cu(II) from wastewater in the ultrafiltration process. Hydrothermally synthesized titanate nanotubes (TNT) was modified with thiol functional groups and then directly incorporated to the polyvinyl chloride nanofiber matrices via electrospinning process to fabricate an adsorptive membrane. The as-prepared electrospun nanofiber membranes and the nanoadsorbents were characterized with respect to the physiochemical properties, surface structure and morphology, applying XPS, FTIR, FESEM, EDX and TEM analysis and then, the membranes were evaluated in terms of the removal of the heavy metal ions in a continuous ultrafiltration mode. In adsorptive filtration of the metal ions, the effective factors including nanoadsorbents loading (0.5–1.5 wt%), initial metal ion concentration (60–150 mg/L), feed temperature (~25 °C–45 °C), presence of competing ion and reusability were investigated in the UF system where the membranes containing 1.5 wt% thiol-modified TNT and virgin TNT adsorbents demonstrated excellent removal efficiency compared to the other membranes. The Cu(II) and Ni(II) removal efficiency of the membrane containing 1.5 wt% functionalized TNT was 90% and 86.7%, respectively which was the highest ones. As was expected and due to the uniform dispersion and less aggregation of the modified TNT adsorbents on the large surface area of the electrospun nanofibers, more adsorption capacity of the nanoparticles can be exploited. Moreover, the strong affinity of the thiol functional groups toward the metal cations, these membranes removed metal contaminants more efficiently. Besides, the Cu(II) removal